鋼種
|
C
|
Si
|
Mn
|
P
|
S
|
Ni
|
Cr
|
Cu
|
N
|
MD30
|
SFE
|
備注
|
LA
|
0.077
|
0.49
|
9.94
|
0.035
|
0.001
|
0.67
|
14.56
|
1.1
|
0.144
|
113.074
|
44.059
|
聯(lián)眾
|
LH
|
0.088
|
0.51
|
9.95
|
0.041
|
0.002
|
0.35
|
14.45
|
1.37
|
0.154
|
106.064
|
45.258
|
聯(lián)眾
|
L1
|
0.073
|
0.61
|
9.3
|
0.046
|
0.002
|
1.12
|
14.41
|
1.43
|
0.148
|
96.589
|
45.285
|
聯(lián)眾
|
L4
|
0.045
|
0.5
|
7.93
|
0.035
|
0.002
|
4.12
|
14.65
|
1.45
|
0.065
|
69.112
|
47.356
|
聯(lián)眾
|
201實際
|
0.09
|
0.6
|
7
|
0.01
|
0.003
|
3.6
|
16.1
|
0
|
0.15
|
52.93
|
32.458
|
ASTM
|
202實際
|
0.09
|
0.6
|
9.5
|
0.02
|
0.002
|
4.1
|
17.2
|
0
|
0.13
|
12.35
|
40.558
|
ASTM
|
D-7
|
0.07
|
0.57
|
5.78
|
0.034
|
0.003
|
2.42
|
17.16
|
2.43
|
0.1
|
44.656
|
40.920
|
NTK
|
D-11
|
0.06
|
0.6
|
5.69
|
0.032
|
0.002
|
3.6
|
17.34
|
2.15
|
0.1
|
21.163
|
41.211
|
NTK
|
ASTM304
|
0.05
|
0.45
|
1.1
|
0.02
|
0.001
|
8.02
|
18.1
|
0
|
0.05
|
-11.9
|
21.414
|
ASTM
|
1)Md30(℃):在原料上施加 30% true strain時,生成50%形變martensite(α’)的溫度。此溫度越高(Low Ni%),γ相的穩(wěn)定性低,生成martensite量越多。為了確保產(chǎn)品的成形性, 304鋼管理范圍 一般是-5±10℃。
2)SFE:此數(shù)值高的材料變形時因交叉Slip發(fā)生,成形時加工硬化度低,所以加工性提高。Cu大約比Ni的SFE 高2倍。
從上表中的Md30的數(shù)據(jù)進行分析:隨著Ni和Cu的含量增加,鋼種的Md30減小,有利于不銹鋼的加工;從上表中的SFE的數(shù)據(jù)進行分析,隨著Ni、Cu和Mn的含量增加,有利于不銹鋼的加工。
2、力學(xué)性能:
鋼種 | YS | TS | HV | EL | 抗彎性 (R=t,180°) |
備注 |
LA | 407 | 880 | 230 | 46 | 無裂縫 | 聯(lián)眾 |
LH | 408 | 895 | 220 | 48 | 無裂縫 | 聯(lián)眾 |
L1 | 385 | 790 | 223 | 51 | 無裂縫 | 聯(lián)眾 |
L4 | 343 | 665 | 190 | 51 | 無裂縫 | 聯(lián)眾 |
201實際 | 390 | 720 | 210 | 45 | 無裂縫 | ASTM |
202實際 | 356 | 680 | 183 | 50 | 無裂縫 | ASTM |
D-7 | 409 | 727 | 202 | 45 | 無裂縫 | NTK |
D-11 | 360 | 691 | 180 | 47 | 無裂縫 | NTK |
ASTM304 | 320 | 680 | 165 | 62 | 無裂縫 | ASTM |
從上表中可以得知:EL的數(shù)值大的鋼種有利于加工。